APICAL
Type AF Polyimide Film
| Property |
120AF616 |
130AF616B |
150AF019 |
250AF029 |
200AF919 |
300AF929 |
Method |
| Dielectric
Strength, AC V/mil (k V/mm) (Minimum) |
5,000
(197)
|
5,000
(197)
|
4,000
(158)
|
4,000
(158)
|
3,000
(118)
|
3,000
(118)
|
ASTM
D-149, Flat sheet in air placed between 1/4" (6.35mm)
diameter brass electrodes with 1/32" (0.8mm) edge
radius subjected to 60 cycles AC voltage at 500
volts/sec. rate of rise. |
| Volume
Resistivity, ohm-cm at 200°C (392°F) (Minimum) |
1012
|
1012
|
1012
|
1012
|
1012
|
1012
|
ASTM
D-257 |
| Dielectric
Constant at 1kHz (Maximum) |
3.9
|
3.9
|
3.9
|
3.9
|
3.9
|
3.9
|
ASTM
D-150, Using conducting silver paint electrodes,
two terminal system of measurement at standard conditions. |
| Dissipation
Factor at 1 kHz (Maximum) |
0.0035
|
0.0035
|
0.0035
|
0.0035
|
0.0035
|
0.0035
|
ASTM
D-150, Same as above method. |
| Property |
200AF011 |
300AF021 |
500AF131 |
120AFY616 |
150AFY019 |
Method |
| Dielectric
Strength, AC V/mil (k V/mm) (Minimum) |
3,000
(118)
|
2,500
(98)
|
2,000
(79)
|
5,000
(197)
|
4,000
(157)
|
ASTM
D-149, Flat sheet in air placed between 1/4" (6.35mm)
diameter brass electrodes with 1/32" (0.8mm) edge
radius subjected to 60 cycles AC voltage at 500
volts/sec. rate of rise. |
| Volume
Resistivity, ohm-cm at 200 ° C (392 ° F)
(Minimum) |
1012
|
1012
|
1012
|
1012
|
1012
|
ASTM
D-257 |
| Dielectric
Constant at 1kHz (Maximum) |
3.9
|
3.9
|
3.9
|
3.9
|
3.9
|
ASTM
D-150, Using conducting silver paint electrodes,
two terminal system of measurement at standard conditions. |
| Dissipation
Factor at 1 kHz (Maximum) |
0.0035
|
0.0035
|
0.0035
|
0.0035
|
0.0035
|
ASTM
D-150, Same as above method. |